X-Ray Fractography for (α + γ) Dual Phase Stainless Steels Using Parameter ΔεP Obtained from Micromechanics

Hajime Hirose, Toshihiko Sasaki, Masumi Saka

研究成果: Article査読

1 被引用数 (Scopus)


X-ray diffraction observation of metal fractures provides us with useful information on the mechanisms and mechanical conditions of fracturing. This method has been developed especially as an engineering tool for fracture analysis, (α + γ) dual phase stainless steel JIS-SUS329J4L is a composite material which consists of ferrite αFe and austenite γFe phases. This material excels in corrosion-resistance in the chlorinated environment, and is used for chemical plant and the oil pipes. In this study, X-ray fractogarphy technique is applied to fatigue fracture surface of dual phase stainless steel. Fatigue crack propagation tests were conducted under stress ratios of 0.5 and 0.7. Residual phase and macro stresses near the fracture surface were measured using X-ray diffraction method to the depth direction. In addition, the distribution of the misfit of plastic strain ΔεP between αFe and γFe phase obtained from micro-mechanics beneath the fracture surface was calculated. From the distribution of these X-ray parameters, the depth of the maximum plastic zone ωy was determined. Relations between ωy and fracture mechanics parameter were examined. As the result, ΔεP was related with the maximum stress intensity factor Kmax divided by the 0.2% proof stress σ0.2. Moreover, it is suggested that ΔεP more effective parameter than residual stresses for determination of ωy of dual phase stainless steel.

ジャーナルZairyo/Journal of the Society of Materials Science, Japan
出版ステータスPublished - 2004 2月

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学


「X-Ray Fractography for (α + γ) Dual Phase Stainless Steels Using Parameter ΔεP Obtained from Micromechanics」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。