Wear resistance of SiO2-doped Y-TZP grinding media during wet milling

Hiroshi Ohnishi, Miyuki Takeuchi, Tohru Sekino, Yuichi Ikuhara, Koichi Niihara

研究成果: Article査読

4 被引用数 (Scopus)

抄録

Grinding media 1 mm in diameter, containing 0.4 and 0.7 wt% SiO 2, were fabricated using Y-TZP powder prepared by the liquid-phase method. The wear resistance of media for grinding, with and without the addition of BaTiO3 powder, was evaluated at 20-80°C in water and in a nonaqueous solvent, isoparaffin. A rapid increase in the media wear rate of SiO2-undoped media at 60°C was observed using water as a solvent, but little wear was observed for isoparaffin. The operating time until a rapid increase in the wear rate was observed in water increased with the increase in the grain size of the Y-TZP media. When the media wear became stable, the media surface was observed to be smooth. This suggested that the hydration reaction of Y2O3 and/or ZrO2 by OH- was inhibited by an increase in the grain size, and as a consequence, the decay of the grain boundaries was suppressed. In contrast, several traces of grain loss from the grain boundaries were confirmed on the worn surface of the media when a rapid increase in the wear rate was observed. The wear resistance for grinding BaTiO3 powder using SiO2-doped and -undoped media was also investigated. The wear for SiO2-undoped media increased drastically with increasing slurry temperature; however, the wear for SiO2-doped media did not increase, but was low and stable, regardless of the slurry temperature. This indicated that the hydration reaction of Y2O 3 and/or ZrO2 by OH- was further inhibited by the segregation of SiO2 at the grain boundaries, and hence SiO 2-doped Y-TZP media have high wear resistance, even with increased slurry temperature.

本文言語English
ページ(範囲)502-511
ページ数10
ジャーナルInternational Journal of Applied Ceramic Technology
7
4
DOI
出版ステータスPublished - 2010 7 1

ASJC Scopus subject areas

  • セラミックおよび複合材料
  • 凝縮系物理学
  • マーケティング
  • 材料化学

フィンガープリント

「Wear resistance of SiO<sub>2</sub>-doped Y-TZP grinding media during wet milling」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル