Viscosity measurement of molten RE-Mg-Si-O-N (RE=Y, Gd, Nd and La) glasses

Noritaka Saito, Daiji Nakata, Sohei Sukenaga, Kunihiko Nakashima

研究成果: Article査読

2 被引用数 (Scopus)

抄録

Viscosities of molten RE-Mg-Si-O-N (RE=Y, Gd, Nd and La) glasses have been measured using rotating bob viscometer with a gas tight furnace at elevated temperature (∼1873 K). Moreover, structural characterizations of these quenched vitreous samples have been investigated using solid state 29Si MAS-NMR, which would resolve the relationship between the viscosity of high temperature melts and network structure of RE-Mg-Si-O-N systems. The viscosities of molten RE-Mg-Si-O-N glasses exponentially increased with nitrogen content. 29Si MAS-NMR spectra of RE-Mg-Si-O-N (RE=Y and La) glasses revealed that content of silicon-oxynitride species, like SiO 3N, increased with nitrogen content, which indicates that nitrogen clearly modifies the glass network structure. Depending on cationic radius of rare-earth elements, Y was found to be more effective in silicon-oxynitride species formation than La, which are consistent with the results of viscosity measurement of molten RE-Mg-Si-O-N glasses at elevated temperature (∼1873 K).

本文言語English
ページ(範囲)69-72
ページ数4
ジャーナルKey Engineering Materials
403
DOI
出版ステータスPublished - 2009
外部発表はい

ASJC Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Viscosity measurement of molten RE-Mg-Si-O-N (RE=Y, Gd, Nd and La) glasses」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル