Use of an Abrasive Water Cavitating Jet and Peening Process to Improve the Fatigue Strength of Titanium Alloy 6Al-4V Manufactured by the Electron Beam Powder Bed Melting (EBPB) Additive Manufacturing Method

Hitoshi Soyama, Daniel Sanders

研究成果: Article査読

10 被引用数 (Scopus)

抄録

Metal components made by additive manufacturing have large inherent surface roughness, and, as such, their strength and fatigue life can be reduced significantly versus wrought products. In order to improve these properties, a novel mechanical surface treatment that introduces compressive residual stress while simultaneously reducing the surface roughness is proposed. The proposed treatment uses cavitation peening combined with an abrasive slurry. The impact of the kinetic energy-charged abrasive particles, induced by collapsing water cavitation vapor bubbles, produces compressive residual stress, while the abrasive reduces the surface roughness. Plane-bending fatigue tests were carried out to determine the effectiveness of this treatment on the fatigue life and strength of titanium alloy Ti6Al4V manufactured by electron beam melting. It was demonstrated that the fatigue strength of an as-built specimen was improved from 169 MPa to 280 MPa by the proposed treatment.

本文言語English
ページ(範囲)4311-4318
ページ数8
ジャーナルJOM
71
12
DOI
出版ステータスPublished - 2019 12 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Engineering(all)

フィンガープリント 「Use of an Abrasive Water Cavitating Jet and Peening Process to Improve the Fatigue Strength of Titanium Alloy 6Al-4V Manufactured by the Electron Beam Powder Bed Melting (EBPB) Additive Manufacturing Method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル