Ultra-low-damage radical treatment for the highly controllable oxidation of large-scale graphene sheets

Chi Hsien Huang, Ching Yuan Su, Chao Sung Lai, Yen Cheng Li, Seiji Samukawa

研究成果: Article査読

27 被引用数 (Scopus)

抄録

We have used low-damage oxygen radical treatment (O-LDRT) - with chemically reactive radicals generated in a plasma system equipped with a complementary filter - to prepare large-scale graphene oxide sheets with highly controllable levels of oxidation. Raman spectroscopy and X-ray photoelectron spectroscopy revealed that oxidative functionalities were formed on the graphene surfaces in a highly controllable manner and with a wide process window. Contact angle measurements revealed the high hydrophilicity of the large-scale graphene after O-LDRT. We measured the current-voltage characteristics of oxidized double-layer graphene (DLG) sheets to confirm the low degree of damage after using O-LDRT for the oxidation process. For treatment times of up to 5 min, the current passing through the DLG sheets remained almost identical to that passing through the corresponding sample that had not been subjected to O-LDRT, indicating that the bottom layer of the graphene sheet remained almost unmodified, whereas a massive number of oxidative functionalities had been formed on the top layer of the graphene sheet; in addition, the adhesion energy increased to approximately twice that of the untreated graphene sheet.

本文言語English
ページ(範囲)244-251
ページ数8
ジャーナルCarbon
73
DOI
出版ステータスPublished - 2014 7月

ASJC Scopus subject areas

  • 化学 (全般)
  • 材料科学(全般)

フィンガープリント

「Ultra-low-damage radical treatment for the highly controllable oxidation of large-scale graphene sheets」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル