Three-dimensional periodic structures of gold nanoclusters in the interstices of sub-100 nm polymer particles toward surface-enhanced Raman scattering

Ayumi Yahata, Haruyuki Ishii, Kosuke Nakamura, Kanako Watanabe, Daisuke Nagao

研究成果: Article査読

2 被引用数 (Scopus)

抄録

Regularly ordered polymer nanoparticle (PNP) assemblies incorporating gold nanoparticle (Au NP) clusters into the PNP interstices were fabricated by a simultaneous deposition of PNPs and Au NPs on a glass substrate. Monodisperse PNPs with an average size of 66 nm were employed as a template in the co-assembly to create the sub-100 nm periodic Au nanostructures on the substrate. First, mono-layering of PNP array with incorporation of 14 nm Au NPs was performed by a drop-casting to examine the number ratio of Au NPs to PNPs for multi-layering. Absorption spectra of the mono-layered co-assemblies of PNPs and Au NPs were employed to characterize the clustered state of Au NPs in the interstices of mono-layered PNPs. The number ratio suitable for homogeneous incorporation of Au NPs clustered in the interstice was found to be ranged from 6 to 8 in the characterization. Then, multi-layered co-assemblies of PNPs and clustered Au NPs were fabricated by a vertical deposition method with the Au NP number ratio of 8 to PNPs. Lifting rate of the substrate on which the PNPs were deposited was varied in the vertical deposition method to tune the film thickness of NP co-assembly. A decrease in the lifting rate to 1 μm/s could thicken the film to 0.71 μm corresponding to 13 layers of PNPs, resulting in the fabrication of periodic structures of Au NP clusters with a high packing density. Signal-to-noise ratio in the Raman measurement using p-mercaptobenzoic acid as a target molecule was successfully enhanced by multi-layering of the co-assembly, indicating that Au NP clusters were homogeneously incorporated into the interstices of PNPs in the co-assemblies.

本文言語English
ページ(範囲)2957-2963
ページ数7
ジャーナルAdvanced Powder Technology
30
12
DOI
出版ステータスPublished - 2019 12月

ASJC Scopus subject areas

  • 化学工学(全般)
  • 材料力学

フィンガープリント

「Three-dimensional periodic structures of gold nanoclusters in the interstices of sub-100 nm polymer particles toward surface-enhanced Raman scattering」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル