Thickness-dependent physical properties of La1/3Sr2/3FeO3 thin films grown on SrTiO3 (001) and (111) substrates

Makoto Minohara, Miho Kitamura, Hiroki Wadati, Hironori Nakao, Reiji Kumai, Youichi Murakami, Hiroshi Kumigashira

研究成果: Article査読

4 被引用数 (Scopus)

抄録

We have investigated the thickness-dependent transport properties of La1/3Sr2/3FeO3 thin films grown on SrTiO3 (001) and (111) substrates. At a thickness of ∼40 nm, both films show a clear transition in resistivity associated with the characteristic charge disproportionation at approximately 190 K. The transition temperature of the charge disproportionation is nearly unchanged with decreasing film thickness down to a certain thickness of ∼13 nm for both orientations, while the change in resistivity gradually decreases. Below this thickness, the transition becomes unclear, strongly suggesting the suppression of the charge disproportionation at the critical thickness of ∼13 nm. Furthermore, there is no significant difference in the thickness dependence of La1/3Sr2/3FeO3 thin films between the (001) and (111) orientations. The negligible crystallographic-orientation dependence may reflect the isotropic nature for the domain of charge disproportionation states in La1/3Sr2/3FeO3.

本文言語English
論文番号025303
ジャーナルJournal of Applied Physics
120
2
DOI
出版ステータスPublished - 2016 7 14
外部発表はい

ASJC Scopus subject areas

  • Physics and Astronomy(all)

フィンガープリント 「Thickness-dependent physical properties of La<sub>1/3</sub>Sr<sub>2/3</sub>FeO<sub>3</sub> thin films grown on SrTiO<sub>3</sub> (001) and (111) substrates」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル