The behavior of radiation damage of Nb+ ion implanted sapphire after annealing at reducing atmosphere

N. K. Huang, K. Neubeck, S. Yamamoto, Y. Aoki, H. Abe, K. Narumi, A. Miyashita, H. Naramoto

研究成果: Article査読

10 被引用数 (Scopus)

抄録

Sapphire crystals with (0001) and (0112) orientations were implanted with 380 keV Nb+ ions to a dose of 5 × 1016 ions/cm2 at room temperature and 100 K. The behavior of the radiation damage produced by ion implantation followed by annealing with a series of steps from 500 to 1100°C at reducing atmosphere is investigated using optical absorption technique. The absorption curves were evaluated by Gaussian fitting based on the well known F-type centers, which were confirmed by luminescence measurements. The results of optical density (OD) from the bands with annealing temperature and time show that the annealing behavior of the radiation damage produced by Nb+ ion implantation can be divided into three stages. The first stage is in the range of annealing from 500 to 800 to 900°C; the second is from 900 to 1000°C, the third is one above 1000°C. Defects were annealed within these stages due to different mechanisms which are proposed on the basis of the optical absorption measurements combined with the observation of SEM micrographs and colour variation of the sample after annealing steps with temperature.

本文言語English
ページ(範囲)367-376
ページ数10
ジャーナルPhysica Status Solidi (A) Applied Research
165
2
DOI
出版ステータスPublished - 1998 2

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics

フィンガープリント 「The behavior of radiation damage of Nb<sup>+</sup> ion implanted sapphire after annealing at reducing atmosphere」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル