Tempered microstructure and mechanical properties of ultra-high carbon steel

Shu Qin Shi, Bao Qi Wang, Tadashi Furuhara, T. Maki, Guang Chen

研究成果: Article査読

3 被引用数 (Scopus)

抄録

The microstructure and mechanical properties of quenched in and phaseregion then tempered ultra-high carbon steel studied by using CM200 transmission election microscopy (TEM) and Instron tensile machine. The results show; The microstructure of specimen tempered at 650°C consists of equiaxed ferrite and spheroidal cementite. The yield strength σ0.2 = 1 127 MPa. The tensile strength σb = 1 266 MPa, the uniform elongation δu = 8.26%, the total elongation δt, = 9. 71% , HV=397; In the specimen tempered at 450°C, the ferrite is of the same form as in quenched sample, the tempered carbide is ε carbide, discontinuously precipitated in platelet, σ0.2 = 1 911 MPa, σb 2 028 MPa, δu = δt, = 1.88%, HV=595; In the specimen tempered at 400°C, the ferrite is of the same form again, the tempered carbide is almost precipitated in nets at dislocations no plasticity can be observed, HV=703.

本文言語English
ページ(範囲)38-41
ページ数4
ジャーナルJournal of Iron and Steel Research
18
3
出版ステータスPublished - 2006 3 1
外部発表はい

ASJC Scopus subject areas

  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Tempered microstructure and mechanical properties of ultra-high carbon steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル