Systematic study in mixed valence system Yb4(As1-xSbx)3

Hayuyoshi Aoki, A. Ochiai, T. Suzuki, R. Helfrich, F. Steglich

研究成果: Article査読

30 被引用数 (Scopus)


In Yb pnictides with anti-Th3P4 structure, the valence of Yb decreases from about 2.25 in Yb4As3 to about 2 in Yb4Bi3 with increasing weight of pnictogen. In Yb4As3, charge ordering around 300 K is observed and in the charge ordered phase heavy fermion behavior is seen in spite of extremely low carrier concentration. On the other hand, Yb4Sb3 is a valence fluctuating system. So, to make systematic studies from Yb4As3 to Yb4Sb3 we grew single crystals of Yb4(As1-xSbx)3. With increasing Sb content, the absolute value of the resistivity decreases due to the increase of the number of carriers and the charge ordering temperature decreases reflecting the increase of the screening effect, and at 29% charge ordering seems to disappear. The γ-value, however, is still large even in Sb 29% sample. The large γ-value of Yb4(As1-xSbx)3 is considered to be independent of the carrier concentration.

ジャーナルPhysica B: Condensed Matter
出版ステータスPublished - 1997 2月

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • 電子工学および電気工学


「Systematic study in mixed valence system Yb4(As1-xSbx)3」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。