Synthesis of Fe16N2 compound films by reactive sputtering

H. Shoji, H. Takahashi, M. Kunii, M. Takahashi, T. Wakiyama

研究成果: Article査読

1 被引用数 (Scopus)

抄録

Fe16N2 films (of thickness 3000 angstroms) were fabricated on MgO (001) substrates by the conventional dc facing target sputtering method using a controlled reactive plasma, at an electron temperature of Te = 0.3 eV, an electron density of Ne = 1×1010 cm-3, a deposition rate of 200 angstroms/min and an N2 flow ratio ranging from 10% to 20%. In the as-deposited state, single α′ phases with various nitrogen contents were formed. After annealing at 150 °C for two hours, an α″ phase (≅11 at% N) and an α′ phase (11.1 at% N and 1 to 2 at% N) were formed. The Ms value was nearly the same as for α-Fe (2.2 T), despite the existence of the α″ phase. The lattice constant c of the α″ phase in these films agreed well with the value reported by Jack, but lattice constant a values were about 1 to 3% smaller than Jack's value. The unit cell volumes of the α″ phase in these films were between 192.5 and 202.6 angstroms3, from 1.4 to 6.3% less than Jack's value of 205.5 angstroms3.

本文言語English
ページ(範囲)152-157
ページ数6
ジャーナルIEEE translation journal on magnetics in Japan
9
1
DOI
出版ステータスPublished - 1994 1

ASJC Scopus subject areas

  • Engineering(all)

フィンガープリント 「Synthesis of Fe<sub>16</sub>N<sub>2</sub> compound films by reactive sputtering」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル