Synthesis and long-period phosphorescence of ZnGa2O4:Mn2+ spinel

Kyota Uheda, Takuya Maruyama, Hirotsugu Takizawa, Tadashi Endo

研究成果: Article査読

45 被引用数 (Scopus)

抄録

Novel long-period phosphor ZnGa2O4:Mn2+ was prepared by a conventional solid reaction of ZnO, Ga2O3 and Mn(NO3)2 under conditions of > 1000°C for 24 h in flowing Ar gas. The phosphor had green intense emission peaking at 503.6 nm. The improvement of emission intensity was brought out by the higher temperature processing. This implied that long lifetime phosphorescence was closely related to the formation of vacancies at the Zn2+ sites of the host lattice. The carrier trap level was positioned at 0.71 eV higher than the valence band of host lattice. The possible mechanism for prolonging the emission for a long time was discussed.

本文言語English
ページ(範囲)60-64
ページ数5
ジャーナルJournal of Alloys and Compounds
262-263
DOI
出版ステータスPublished - 1997 11 14

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Synthesis and long-period phosphorescence of ZnGa<sub>2</sub>O<sub>4</sub>:Mn<sup>2+</sup> spinel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル