Synthesis and characterization of single-walled carbon nanotube/silicon carbide composites

G. Yamamoto, K. Yokomizo, M. Omori, Y. Sato, T. Takahashi, T. Hashida, K. Motomiya, A. Okubo, S. Watanabe, K. Tohji

研究成果: Conference contribution

抄録

Single-walled carbon nanotube (SWCNT)/SiC composites were successfully prepared by direct thermal decomposition of polycarbosilane (PCS) precursor. The SWCNT/SiC composites were prepared by the hot-pressing the SWCNTs-PCS (7:3 mass%) mixture at temperatures of 1000, 1400 and 1800°C under a pressure of 120 MPa. The effects of SiC synthesis and processing temperatures on the mechanical properties of the resultant composites were investigated by comparing the experimental data obtained from the SWCNT/SiC composites and the binder-free SWCNT solids. The XRD and TEM-EDS analyses revealed that the β-SiC was successfully prepared through direct thermal decomposition of PCS precursor. The specific modulus and strength of the SWCNT/SiC composites were always about 8 GPa/Mg/m3 and 20 MPa/Mg/m3 higher than those of the binder-free SWCNT solid under identical processing temperatures. Such remarkable stiffening and strengthening by SiC synthesis may be due to the load-transfer efficiency of SWCNTs in the SWCNT/SiC composites.

本文言語English
ホスト出版物のタイトルWATER DYNAMICS
ホスト出版物のサブタイトル3rd International Workshop on Water Dynamics
ページ94-99
ページ数6
DOI
出版ステータスPublished - 2006 5 15
イベントWATER DYANMICS: 3rd International Workshop on Water Dynamics - Sendai, Japan
継続期間: 2005 11 162005 11 17

出版物シリーズ

名前AIP Conference Proceedings
833
ISSN(印刷版)0094-243X
ISSN(電子版)1551-7616

Other

OtherWATER DYANMICS: 3rd International Workshop on Water Dynamics
CountryJapan
CitySendai
Period05/11/1605/11/17

ASJC Scopus subject areas

  • Physics and Astronomy(all)

フィンガープリント 「Synthesis and characterization of single-walled carbon nanotube/silicon carbide composites」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル