Surface damage and radiation resistance of lithium tetraborate single crystals

T. Sugawara, R. Komatsu, Satoshi Uda

研究成果: Article査読

12 被引用数 (Scopus)

抄録

The surface damage thresholds of Li2B4O7 crystals, nonlinear crystals used in ultraviolet (UV) solid-state lasers, were measured and found to be 8.4 GW/cm2 at 1064 nm, 1.9 GW/cm2 at 532 nm, and 0.83 GW/cm2 at 266 nm. The damage threshold at 1064 nm was 1.5 times higher than that of fused silica. In addition, the direction dependence of the damage threshold was {1 1 0}>{0 0 1}>{1 0 0}. No color center was generated in the crystal after 20 W/cm2, 107 shots irradiation of KrF and ArF excimer lasers. The excellent damage threshold and radiation resistance of Li2B4O7 were attributable to its wide band gap and relatively few defects in the crystal.

本文言語English
ページ(範囲)225-229
ページ数5
ジャーナルOptical Materials
13
2
DOI
出版ステータスPublished - 1999 1月 1
外部発表はい

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • コンピュータ サイエンス(全般)
  • 原子分子物理学および光学
  • 分光学
  • 物理化学および理論化学
  • 有機化学
  • 無機化学
  • 電子工学および電気工学

フィンガープリント

「Surface damage and radiation resistance of lithium tetraborate single crystals」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル