Surface composition and anodic polarization behavior of zirconium-based amorphous alloys in a phosphate-buffered saline solution

S. Hiromoto, K. Asami, A. P. Tsai, M. Sumita, T. Hanawa

研究成果: Article査読

18 被引用数 (Scopus)

抄録

5 atom % of zirconium in amorphous Zr65Al7.5Cu27.5 alloy was replaced with various M (Pd, Ni, In, Mn, Cr, Ti, Nb, and Zr), to evaluate the effects of alloying elements, M, on the surface composition and anodic polarization behavior of the alloy. The surface oxide of the Zr-M-Al-Cu alloys generated in a deaerated phosphate-buffered saline solution, PBS(-), was characterized using X-ray photoelectron spectroscopy. Also, the alloy was anodically polarized in deaerated PBS(-) to determine open-circuit potential, Eopen, polarization resistance, Rp, and pitting potential, Epit. M was incorporated into the surface oxide film with the increase in the oxygen affinity of M, and the relative concentration of Zr to Al, [Zr]/[Zr + Al], was varied. The Rp at Eopen increased and Epit decreased with the increase in [Zr]/[Zr + Al]. Therefore, the high value of Rp with the large ratio of [Zr]/[Zr + Al] seems to be caused by the high resistance of Zr-containing oxide to general corrosion and/or the preferential dissolution of Al. Zr-containing oxide is susceptible to pitting corrosion. Eventually, the Rp values of Pd-, Ni-, and Nb-containing alloys were high. The Epit values of Pd-, and In-, Zr-containing alloys were high.

本文言語English
ページ(範囲)B117-B122
ジャーナルJournal of the Electrochemical Society
149
4
DOI
出版ステータスPublished - 2002 4

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Renewable Energy, Sustainability and the Environment
  • Surfaces, Coatings and Films
  • Electrochemistry
  • Materials Chemistry

フィンガープリント 「Surface composition and anodic polarization behavior of zirconium-based amorphous alloys in a phosphate-buffered saline solution」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル