Superplasticity of Cu-Al-Mn-Ni shape memory alloy

Toshihiro Omori, Naoki Koeda, Yuji Suto, Ryosuke Kainuma, Kiyohito Ishida

研究成果: Article

14 引用 (Scopus)

抜粋

The microstructurc and superplastic behavior at 450°C and 500°C in Cu-Al-Mn-based shape memory alloys were investigated using optical microscopy and a tensile test. It was found that a fine α (fcc) + β (bcc) two-phase structure with a grain size of 3 μm in diameter can be obtained in Cu-Al-Mn-Ni alloy by annealing at 600°C. The flow stress of Cu-Al-Mn-Ni alloy depends on the strain rate and the strain rate sensitivity is over 0.3 with an elongation of over several hundred percent, which shows that the Cu-Al-Mn-Ni shape memory alloy exhibits superplasticity. For the test temperature at 500°C and a strain rate of 5 × 10-4 s -1, a maximal elongation of 1150% was obtained. The formation of cavity stringers lying parallel to the tensile axis was observed and the size of the cavity was larger as the specimen was more highly deformed.

元の言語English
ページ(範囲)2914-2918
ページ数5
ジャーナルMaterials Transactions
48
発行部数11
DOI
出版物ステータスPublished - 2007 11 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント Superplasticity of Cu-Al-Mn-Ni shape memory alloy' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用