Superplasticity in large-grained Fe3Al alloys

Dongliang Lin, Aidang Shan, Mingwei Chen

    研究成果: Article査読

    7 被引用数 (Scopus)

    抄録

    The superplasticity behavior of Fe-28Al, Fe-28Al-2Ti, Fe-28Al-4Ti (all composition reported are in atomic percent) alloys has been investigated by tensile testing, optical microscopy and transmission electron microscopy. Tensile test were performed at 700 to 900°C under a strain rate range of about 10-5/s to 10-2/s. Maximum strain rate sensitivity index m was found to be 0.5 and the largest elongation reached 620%. The flow activation energy was measured to be 263kJ/mol for Fe-28Al and 191 kJ/mol for Fe-28Al-2Ti, which are much lower than the creep activation energy generally observed in Fe3Al alloys. After deformation grain size became much finer from about 100 μm to 20-30 μm. As combined with TEM observations, it is suggested that a continuous recrystallization process took place and superplasticity may arise from this process.

    本文言語English
    ページ(範囲)419-429
    ページ数11
    ジャーナルActa Metallurgica Sinica Series A, Physical Metallurgy & Materials Science
    8
    4-6
    出版ステータスPublished - 1995 6 1

    ASJC Scopus subject areas

    • 工学(全般)

    フィンガープリント

    「Superplasticity in large-grained Fe3Al alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル