Superconductivity in Anti-ThCr2Si2-type Er2O2Bi Induced by Incorporation of Excess Oxygen with CaO Oxidant

Kyohei Terakado, Ryosuke Sei, Hideyuki Kawasoko, Takashi Koretsune, Daichi Oka, Tetsuya Hasegawa, Tomoteru Fukumura

研究成果: Article査読

9 被引用数 (Scopus)

抄録

Recently, superconductivity was induced by expanding interlayer distance between Bi square nets in anti-ThCr2Si2-type Y2O2Bi through incorporation of excess oxygen with increased nominal amount of oxygen. However, such oxygen incorporation was applicable to only Y2O2Bi among R2O2Bi (R = rare earth metal), probably due to a larger amount of oxygen incorporation for Y2O2Bi. In this study, the interlayer distance in Er2O2Bi was increased by cosintering with CaO, which served as an oxidant, indicating that excess oxygen was incorporated in Er2O2Bi. As a result, superconductivity was induced in Er2O2Bi at 2.2 K.

本文言語English
ページ(範囲)10587-10590
ページ数4
ジャーナルInorganic chemistry
57
17
DOI
出版ステータスPublished - 2018 9 4

ASJC Scopus subject areas

  • 物理化学および理論化学
  • 無機化学

フィンガープリント

「Superconductivity in Anti-ThCr<sub>2</sub>Si<sub>2</sub>-type Er<sub>2</sub>O<sub>2</sub>Bi Induced by Incorporation of Excess Oxygen with CaO Oxidant」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル