STUDIES ON TEMPERATURE-RATE SENSITIVITY OF PLASTIC FLOW STRESSES AND ON FRACTURE TOUGHNESS.

G. S. Pisarenko, A. J. Krasowsky, T. Yokobori

    研究成果: Article査読

    9 被引用数 (Scopus)

    抄録

    A study was carried out on aluminum killed hot-rolled plain, low-carbon steel, for the purpose of assessing the process of plastic strain zone evolution during loading of the specimen with a crack. All specimens were manufactured from sheet iron of one and the same heat, the sheet thickness being of 3. 1 mm. They were heated at 1030 degree C for 2 hours and cooled at a cooling rate of 60 degree C/hr in vaccuum furnace. An evaluation of parameters of plastic strain is made. Temperature and rate dependences of fracture toughness are analyzed.

    本文言語English
    ページ(範囲)1-57
    ページ数57
    ジャーナルRep Res Inst Strength Fract Mater Tohoku Univ
    13
    1
    出版ステータスPublished - 1977 1 1

    ASJC Scopus subject areas

    • Engineering(all)

    フィンガープリント 「STUDIES ON TEMPERATURE-RATE SENSITIVITY OF PLASTIC FLOW STRESSES AND ON FRACTURE TOUGHNESS.」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル