Structural transformation of ca-arrangements and carrier transport properties in Ca0.33CoO2 epitaxial films

Kenji Sugiura, Hiromichi Ohta, Yukiaki Ishida, Rong Huang, Tomohiro Saito, Yuichi Ikuhara, Kenji Nomura, Hideo Hosono, Kunihito Koumoto

    研究成果: Article査読

    11 被引用数 (Scopus)

    抄録

    The electrical properties of Ca0.33CoO2 epitaxial films are investigated as the Ca2+-arrangement is transformed. Despite identical Ca-content, annealing the film caused the Ca-arrangement to change from a <!-Math-> hexagonal type to a 2a × <!-Math-> orthorhombic type, which was confirmed by X-ray diffraction and scanning transmission electron microscopy. A hexagonal Ca-arrangement type, Ca 0.33CoO2, exhibited a metallic resistivity as low as 7.5 × 10-4 Ω·cm and a moderately large thermopower (̃100μV·K-1), whereas the orthorhombic Ca-arrangement type displayed a thermally-activated resistivity (10-2 Ω·cm) with a slightly increase in thermopower, which led to about a one order of magnitude difference in the thermoelectric power factor.

    本文言語English
    論文番号035503
    ジャーナルApplied Physics Express
    2
    3
    DOI
    出版ステータスPublished - 2009 3 1

    ASJC Scopus subject areas

    • 工学(全般)
    • 物理学および天文学(全般)

    フィンガープリント

    「Structural transformation of ca-arrangements and carrier transport properties in Ca<sub>0.33</sub>CoO<sub>2</sub> epitaxial films」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル