Structural and characteristic variation of anodic oxide on pure Ti with anodization duration

Yoshiteru Mizukoshi, Naofhumi Ohtsu, Naoya Masahashi

研究成果: Article査読

16 被引用数 (Scopus)

抄録

Change in the structural and characteristic of the anodic oxide on pure Ti with the duration of anodization time was investigated. With the progress of the anodization, the phase of the formed TiO 2 successively changed from anatase phase to rutile phase. In the transition process, peak intensities of rutile TiO 2 1 0 1, 1 1 1 and 2 1 1 planes of X-ray diffraction characteristically increased. The contact angles of water droplets on the anodize TiO 2 were monotonously decreased with the progress of the anodization except on the characteristically oriented rutile surface. In the evaluations of acetaldehyde photocatalysis under UV illumination, the anatase TiO 2 anodized for short period exhibited high activities. On the other hand, when illuminated with visible light (>422 nm), rutile-structured TiO 2 formed by anodization with a long duration exhibited superior photocatalytic activities probably due to high rutile fraction and sulfur incorporation from the electrolyte.

本文言語English
ページ(範囲)1018-1023
ページ数6
ジャーナルApplied Surface Science
283
DOI
出版ステータスPublished - 2013 10 15
外部発表はい

ASJC Scopus subject areas

  • 化学 (全般)
  • 凝縮系物理学
  • 物理学および天文学(全般)
  • 表面および界面
  • 表面、皮膜および薄膜

フィンガープリント

「Structural and characteristic variation of anodic oxide on pure Ti with anodization duration」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル