Structural and antiferromagnetic characterization of noncollinear D019 Mn3Ge polycrystalline film

Takahiro Ogasawara, Jun young Kim, Yasuo Ando, Atsufumi Hirohata

研究成果: Article査読

8 被引用数 (Scopus)

抄録

Distorted Heusler compound of D019 Mn3Ge polycrystalline films were studied in terms of their crystalline structures and antiferromagnetic behavior by varying annealing temperature and Mn-Ge composition. Although low temperature growth for 30 nm Mn3Ge showed no diffraction peaks in X-ray diffraction patterns, high temperature growth over 773 K with Mn-rich composition is found to promote the (0001) orientation of D019 Mn3Ge which resulted in the emergence of an exchange bias effect in Co0.6Fe0.4 ferromagnetic layer at 120 K. The exchange bias field of 12 Oe in Mn3.16Ge film grown at 773 K were improved to 61 Oe by enriching Mn composition to Mn3.97Ge. The average blocking temperature was measured to be at 150 K which is not as high as its reported Néel temperature of 390 K in the bulk state, however, further improvements are expected by doping additional transition elements.

本文言語English
ページ(範囲)7-11
ページ数5
ジャーナルJournal of Magnetism and Magnetic Materials
473
DOI
出版ステータスPublished - 2019 3 1

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学

フィンガープリント

「Structural and antiferromagnetic characterization of noncollinear D0<sub>19</sub> Mn<sub>3</sub>Ge polycrystalline film」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル