Storage and release of soluble hexavalent chromium from chromate conversion coatings. Equilibrium aspects of CrVI concentration

Lin Xia, Ejii Akiyama, Gerald Frankel, Richard McCreery

研究成果: Article査読

187 被引用数 (Scopus)


The release of soluble CrVI species by a chromate conversion coating (CCC) was monitored quantitatively by ultraviolet-visible spectroscopy. By careful selection of measurement wavelength (339 nm), the CrVI concentration could be determined without regard to solution pH or CrVI speciation. The CrVI concentration in solution over a CCC reached an equilibrium value that depended on pH, ionic strength, and the ratio of the CCC surface area to the solution volume (A/V). In separate experiments, the adsorption of CrVI by synthetic CrIII hydroxide to form a CrIII-CrVI mixed oxide was observed, and also led to an equilibrium concentration of CrVI in solution. The equilibrium CrVI concentration was determined for a variety of A/V values on both AA1100 and AA2024-T3 aluminum alloys. The results are inconsistent with release mechanisms based on the solubility of a CrVI salt in the solution or depletion of CrVI from the CCC. However, the observed concentrations are consistent with a mechanism similar to a Langmuirian adsorption-desorption equilibrium of CrVI on a porous, insoluble CrIII hydroxide matrix. The CrIII hydroxide matrix has a finite number of CrVI binding sites and exhibits a nonlinear relationship between solution and solid CrVI concentrations governed by an equation similar to a Langmuir adsorption isotherm. The proposed model incorporates reversible adsorption and desorption of CrVI, with adsorption favored at low pH during formation of the CCC, and desorption favored in field conditions. The model quantitatively predicts the observed concentrations after determining the binding constant from fits to the data. The model explains the capacity of a CCC to release active CrVI corrosion inhibitor and provides strong evidence that CrVI storage in a CCC involves reversible formation of a CrVI-O-CrIII mixed oxide.

ジャーナルJournal of the Electrochemical Society
出版ステータスPublished - 2000 7月

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 再生可能エネルギー、持続可能性、環境
  • 表面、皮膜および薄膜
  • 電気化学
  • 材料化学


「Storage and release of soluble hexavalent chromium from chromate conversion coatings. Equilibrium aspects of CrVI concentration」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。