自動車用超高強度 TRIP 型マルテンサイト鋼板のスポット溶接引張特性

Akihiko Nagasaka, Tomohiko Hojo, Katsuya Aoki, Hirofumi Koyama, Akihiro Shimizu

研究成果: Article査読

1 被引用数 (Scopus)

抄録

Effect of heat-affected zone (HAZ) softening on tensile strength (TS) and total elongation (TEl) of spot welded ultrahigh strength TRIP-aided martensitic (TM) steel sheet was investigated for automobile applications. Tensile test was performed on an Instron type tensile testing machine at a crosshead speed of 3 mm/min (strain rate of 8.3×10-4 s-1), using spot welded specimen. The results are as follows. (1) The spot welded specimen at the current value (I) of 6.5 kA for the TM steel with the maximum stress (TS*) of 1450 MPa and the fracture elongation (TEl*) of 7.0% was superior to that of hot stamping steel (the HS1 steel), and it was found that the TS* and the TEl* for the TM steel possessed those of base metal specimen for the HS1 steel with the tensile strength (TS) of 1469 MPa and the total elongation (TEl) of 7.7%. (2) The TRIP effect for the TM steel with an excellent strength-ductility balance (TS×TEl) of 14.4 GPa% (i.e. the tensile strength (TS) of 1532 MPa and the total elongation (TEl) of 9.4%) suppressed HAZ softening and was able to express a high maximum stress (TS*) of 1450 MPa for the TM steel of the spot welded specimen.

寄稿の翻訳タイトルSpot welded tensile properties in automobile ultrahigh strength trip-aided martensitic steel sheet
本文言語Japanese
ページ(範囲)438-447
ページ数10
ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
106
7
DOI
出版ステータスPublished - 2020 7 1

Keywords

  • Acoustic emission
  • Hot stamping
  • Spot weldability
  • TRIP
  • Tensile strength

ASJC Scopus subject areas

  • 凝縮系物理学
  • 物理化学および理論化学
  • 金属および合金
  • 材料化学

フィンガープリント

「自動車用超高強度 TRIP 型マルテンサイト鋼板のスポット溶接引張特性」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル