Solid-state diffusion bonding of high-Cr ODS ferritic steel

Sanghoon Noh, Ryuta Kasada, Akihiko Kimura

研究成果: Article査読

50 被引用数 (Scopus)

抄録

Solid-state diffusion bonding (SSDB) was employed to join high-Cr oxide dispersion strengthened (ODS) ferritic steel (Fe-15Cr-2W-0.2Ti-0.35Y 2O3) blocks under uniaxial hydrostatic pressure using a high-vacuum hot press, and the microstructure and mechanical properties of the joints were investigated. High-Cr ODS ferritic steels were successfully diffusion bonded at 1200 °C for 1 h, without precipitates and microvoids at the bonding interface or degradation in the base materials. Transmission electron microscopic observation revealed that the nano-oxide particles near the bonding interface were uniformly distributed in the matrix and that the chemical composition across the bonding interface was virtually constant. At room temperature, the joint had nearly the same tensile properties and exhibited anisotropic behavior similar to that of the base material. The tensile strength of the joint region at elevated temperatures is nearly the same as that of the base material, with necking behavior at several micrometers from the bonding interface. The total elongation of the joint region decreased slightly at 700 °C, with an exfoliation fracture surface at the bonding interface. Although a small ductile-brittle transition temperature shift was observed in the joints, the upper shelf energy was fully reserved in the case of joints with L-R bonding orientation, for which cracks did not propagate on the bonding interface. Therefore, it is concluded that SSDB can be potentially employed as a joining method for high-Cr ODS ferritic steel owing to the excellent mechanical properties of the joints.

本文言語English
ページ(範囲)3196-3204
ページ数9
ジャーナルActa Materialia
59
8
DOI
出版ステータスPublished - 2011 5月
外部発表はい

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • セラミックおよび複合材料
  • ポリマーおよびプラスチック
  • 金属および合金

フィンガープリント

「Solid-state diffusion bonding of high-Cr ODS ferritic steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル