Size Effect on Crystal Structures of Barium Titanate Nanoparticles Prepared by a Sol-Gel Method

Yoshio Kobayashi, Ayako Nishikata, Tomokazu Tanase, Mikio Konno

研究成果: Article査読

51 被引用数 (Scopus)

抄録

Barium titanate nanoparticles were synthesized by the hydrolysis of complex alkoxide precursor that was prepared in a reflux of metallic barium and tetraethylorthotitanate in solvent. The hydrolysis was performed by the addition of water/ethanol solution to the precursor solution. As reflux time increased, particle sizes, which were measured with transmittance electromicroscopy, became smaller followed by sharpening of size distribution. As water concentration and benzene content in the hydrolysis increased, the particle size increased with crystallite size that was determined with X-ray diffractometry. No significant difference was observed between the particle and crystallite sizes up to 30 nm. Over the size of 30 nm, the particle size was larger than the crystallite size because of generation of polycrystallites. Annealing treatments in air at 400 and 1000°C also increased both the particle and crystallite sizes. The crystallite sizes estimated from the (111) peaks were smaller than those from (110) peaks in a range of sizes larger than 40 nm, which indicated that the critical crystallite size of transformation from cubic to tetragonal structures was approximately 40 nm.

本文言語English
ページ(範囲)49-55
ページ数7
ジャーナルJournal of Sol-Gel Science and Technology
29
1
DOI
出版ステータスPublished - 2004 1

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • セラミックおよび複合材料
  • 化学 (全般)
  • 生体材料
  • 凝縮系物理学
  • 材料化学

フィンガープリント

「Size Effect on Crystal Structures of Barium Titanate Nanoparticles Prepared by a Sol-Gel Method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル