Sintering and mechanical properties of Y-TZP/SiC composites

Shinya Terauchi, Tsugio Sato, Tadashi Endo, Masahiko Shimada

研究成果: Article査読

抄録

Zirconia powders containing 3mol% Y2O3 were mixed with SiC powders or SiC whiskers by ball-milling and were uniaxially pressed at 10MPa prior to cold isostatic pressing at 200MPa. The green bodies were sintered at 1450 and 1500°C for 1-18 hours under a stream of 95vol%He-5vol%CO gas, and then were hot isostatically pressed at 1450°C and 150MPa for 1 hour in an Ar gas atmosphere. The density of HIPed bodies increased with increasing that of presintered bodies. The presintered bodies of Y-TZP/2.5vol%SiC particle composites with a relative density above 93% could be densified to almost fully theoretical density by HIPing. The bending strength of the Y-TZP/SiC(particle) and Y-TZP/SiC(whisker) composites increased by hot isostatic pressing, while the values of the Weibull modulus did not increase.

本文言語English
ページ(範囲)1063-1066
ページ数4
ジャーナルFuntai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
37
7
出版ステータスPublished - 1990 9
外部発表はい

ASJC Scopus subject areas

  • Mechanical Engineering
  • Metals and Alloys

フィンガープリント 「Sintering and mechanical properties of Y-TZP/SiC composites」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル