Scintillation and dosimeter properties of LiAlSi2O6 and LiAlSi4O10 crystals

Takayuki Yanagida, Yutaka Fujimoto, Masanori Koshimizu, Narumi Kumamoto, Go Okada, Noriaki Kawaguchi

研究成果: Article査読

1 被引用数 (Scopus)

抄録

Optical, scintillation, optically stimulated luminescence, and thermally stimulated luminescence properties of nondoped LiAlSi2O6 and LiAlSi4O10 mineral crystals were investigated. The photoluminescence emission wavelengths of LiAlSi2O6 and LiAlSi4O10 were 300-500 and 350-600 nm, respectively, and the scintillation emission wavelengths were similar. Under vacuum ultraviolet photon excitation at a synchrotron facility (UVSOR), excitation bands of LiAlSi2O6 and LiAlSi4O10 appeared at around 150 and 180 nm, respectively. The decay lifetime of LiAlSi2O6 was on the nanosecond order while that of LiAlSi4O10 was on the millisecond order for both photoluminescence and scintillation. Both samples showed thermally stimulated luminescence, and LiAlSi4O10 had a higher sensitivity. When we investigated optically stimulated luminescence, LiAlSi4O10 exhibited a detectable signal, while we could not observe a signal in LiAlSi2O6.

本文言語English
ページ(範囲)1399-1406
ページ数8
ジャーナルSensors and Materials
29
10
DOI
出版ステータスPublished - 2017

ASJC Scopus subject areas

  • 器械工学
  • 材料科学(全般)

フィンガープリント

「Scintillation and dosimeter properties of LiAlSi<sub>2</sub>O<sub>6</sub> and LiAlSi<sub>4</sub>O<sub>10</sub> crystals」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル