Room and low temperature direct three-dimensional-strain measurements by neutron diffraction on as-reacted and prebent CuNb Nb3 Sn wire

H. Oguro, S. Awaji, G. Nishijima, P. Badica, K. Watanabe, F. Shikanai, T. Kamiyama, K. Katagiri

研究成果: Article査読

33 被引用数 (Scopus)

抄録

We measured directly by neutron diffraction the axial and lateral residual strains for the prebent and the as-reacted CuNb Nb3 Sn wires at room temperature and at 7 K, in order to investigate the change of the residual strain with prebending treatment. In the axial direction of the wire, the residual strain was changed with 0.20% to the tensile side when measured at both temperatures, while in the lateral direction, the change was 0.08% and 0.03% to the compressive side for the measurements at RT and 7 K, respectively. From the obtained data, we estimated the deviatoric strain. At 7 K, the value is 0.40% for the as-reacted wires and it reduces to 0.19% when the prebending is applied with a strain εpb =0.8%. These results suggest that the reduction of the residual strain in the axial direction as well as in the lateral direction, i.e., of the deviatoric strain is responsible for the observed enhancement in the superconducting properties of the prebent Nb3 Sn wires. In addition, we succeeded in the quantitative evaluation of the deviatoric strain dependence of the upper critical field for the practical Nb3 Sn wire. This is very important for the understanding of the general axial strain dependence of the superconducting properties.

本文言語English
論文番号103913
ジャーナルJournal of Applied Physics
101
10
DOI
出版ステータスPublished - 2007

ASJC Scopus subject areas

  • 物理学および天文学(全般)

フィンガープリント

「Room and low temperature direct three-dimensional-strain measurements by neutron diffraction on as-reacted and prebent CuNb Nb3 Sn wire」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル