Role of cementite and retained austenite on austenite reversion from martensite and bainite in Fe-2Mn-1.5Si-0.3C alloy

Xianguang Zhang, Goro Miyamoto, Yuki Toji, Yongjie Zhang, Tadashi Furuhara

研究成果: Article査読

抄録

The effects of cementite (θ) and retained austenite (RA) on the kinetics and microstructure evolution in austenite (γ) reversion of an Fe-2Mn-1.5Si-0.3C (mass%) alloy have been studied by investigating the reversion from as-quenched and tempered martensite, and bainite. Pre-tempering of martensite or prolonged austempering, both resulting in θ precipitation, enhanced the formation of globular γ at high reversion temperature, while the presence of RA in carbide-free bainite structure obtained by short time austempering suppressed its formation. High-temperature pre-tempering or prolonged austempering retarded the reversion kinetics, while low-temperature pre-tempering or the presence of RA have negligible influences on the kinetics. Nucleation of γ at θ / ferrite interface results in the formation of globular γ. Theoretical analysis reveals that coarser θ particle has a higher nucleation potency for globular γ, and thus coarsening of θ particles by pre-tempering or austempering promotes its formation. On the other hand, the precipitation of θ particles before γ reversion is suppressed when a large amount of RA is present, thus globular γ formation is suppressed. It was concluded that the retardation on reversion kinetics by high-temperature pre-tempering or austempering is mainly owing to the suppression on the growth of reverted γ because of enhanced Mn enrichment into θ and coarsened θ particle.

本文言語English
論文番号116772
ジャーナルActa Materialia
209
DOI
出版ステータスPublished - 2021 5 1

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • セラミックおよび複合材料
  • ポリマーおよびプラスチック
  • 金属および合金

フィンガープリント

「Role of cementite and retained austenite on austenite reversion from martensite and bainite in Fe-2Mn-1.5Si-0.3C alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル