Robust Giant Tetragonal Distortion Coupled with High-Spin Co3+ in Electron-Doped BiCoO3

Hayato Ishizaki, Hajime Yamamoto, Takumi Nishikubo, Yuki Sakai, Shogo Kawaguchi, Keisuke Yokoyama, Yoichi Okimoto, Shin Ya Koshihara, Takafumi Yamamoto, Masaki Azuma

研究成果: Article査読

6 被引用数 (Scopus)

抄録

BiCoO3 is a PbTiO3 type of perovskite oxide with a giant tetragonal distortion (c/a = 1.27) that shows a pressure-induced transition from tetragonal to orthorhombic phases accompanied by a large volume shrinkage at 3 GPa. In this study, we carried out electron doping of BiCoO3 by substituting Ti4+ for Co3+ in order to destabilize the tetragonal phase and observe a giant negative thermal expansion (NTE) at ambient pressure. BiCo1-xTixO3 (x = 0, 0.1, 0.2, and 0.25) was successfully obtained by using high-pressure synthesis. However, the c/a ratio of the tetragonal phase was almost constant against x (≤0.2), and NTE was not observed at any x, suggesting that the tetragonal distortion coupled with high-spin Co3+ is robust against electron doping. In x = 0.25, a metastable orthorhombic phase was obtained by the high-pressure synthetic process, while it partially transformed into a tetragonal phase after annealing at 600 K. The stability of the giant tetragonal phase is strongly connected with the spin state of Co3+.

本文言語English
ページ(範囲)16059-16064
ページ数6
ジャーナルInorganic chemistry
58
23
DOI
出版ステータスPublished - 2019 12 2

ASJC Scopus subject areas

  • Physical and Theoretical Chemistry
  • Inorganic Chemistry

フィンガープリント 「Robust Giant Tetragonal Distortion Coupled with High-Spin Co<sup>3+</sup> in Electron-Doped BiCoO<sub>3</sub>」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル