Residual stress in zirconia coating by EB-PVD method

Kenji Suzuki, Kunihiko Wada, Hideaki Matsubara, Takahisa Shobu, Masashi Kawamura, Keisuke Tanaka

研究成果: Article査読

7 被引用数 (Scopus)

抄録

The Ni-based superalloy IN738LC was used as the substrate material, and CoNiCrAlY powder was pressureless plasma-sprayed on the substrate as the bond coating. Zirconia was coated as the top coating by the electron beam-physical vapor deposition (EB-PVD) method. In the EB-PVD process, the specimens were kept at 1223K and rotated with 5rpm, 10rpm and 20rpm. According to the microscopic observation and the result of the pole figures, the top coatings had a columnar structure, which was made by the piling up of (111) planes. The cross section of the column had a diamond shape, and its diagonal was parallel to the rotation axis. The residual stress on the surface of the top coatings was evaluated by the X-ray diffraction method. Each diffraction profile was separated into the 133 and the 331peak, and the residual stress was measured by the sin 2ψ method. The measured residual stresses were -76.7MPa for 5rpm, -63.0MPa for 10rpm and -25.1MPa for 20rpm.

本文言語English
ページ(範囲)588-593
ページ数6
ジャーナルZairyo/Journal of the Society of Materials Science, Japan
56
7
DOI
出版ステータスPublished - 2007 7

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Residual stress in zirconia coating by EB-PVD method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル