Remarkable Effects of Lanthanide Substitution for the Y-Site on the Oxygen Storage/Release Performance of YMnO3+δ

Mayu Otomo, Takuya Hasegawa, Yusuke Asakura, Shu Yin

研究成果: Article査読

抄録

Lanthanide-substituted YMnO3+δ nanoparticles with the hexagonal phase, denoted as R0.25Y0.75MnO3+δ (R = Er, Dy, Tb, Gd, and Sm), have been successfully synthesized by the polymerized complex method. The substitutions did not largely affect the morphologies and specific surface area of the obtained R0.25Y0.75MnO3+δ nanoparticles. From the evaluation for the oxygen storage/release properties, the oxygen storage capacity (OSC) increased significantly by the Tb substitution, and the oxygen absorption/release rate strongly depended on the ion size of the substituted lanthanides. It was found that Tb4+ existed in Tb0.25Y0.75MnO3+δ after oxygen absorption, demonstrating that the remarkable increase in the OSC of the Tb-substituted sample was due to the oxidation of not only Mn3+ to Mn4+ but also Tb3+ to Tb4+. In addition, the unit cell volume increasing with the R ion size, which can lead to the promotion of the oxygen diffusion in the crystal structure, was the factor leading to the increase of the oxygen absorption rate. Especially, Sm0.25Y0.75MnO3+δ showed an excellent OSC of 3 + δ= 3.34 (the weight increase rate was 2.64 wt %) even under a rapid temperature swing rate of 20 °C/min.

本文言語English
ページ(範囲)31691-31698
ページ数8
ジャーナルACS Applied Materials and Interfaces
13
27
DOI
出版ステータスPublished - 2021 7 14

ASJC Scopus subject areas

  • 材料科学(全般)

フィンガープリント

「Remarkable Effects of Lanthanide Substitution for the Y-Site on the Oxygen Storage/Release Performance of YMnO<sub>3+δ</sub>」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル