Reduction of iron loss in thin grain-oriented silicon steel sheets

M. Nakano, K. Ishiyama, K. I. Aral, H. Fukunaga

研究成果: Article査読

9 被引用数 (Scopus)

抄録

-We investigated the effect of the intermediate annealing conditions on the grain textures and the magnetic properties in thin grain-oriented silicon steel sheets produced by the three-stage rolling method. It was found that the lower the intermediate an- nealing temperature is, the better the[001] orientation is achieved. In addition, the reduction of the intermediate annealing tempera- tures improves dc magnetic properties (Bg, He) and enables to reduce the iron loss in thin silicon steels. The measured iron loss W13/50 under the applied tensile strength of 2 kg/mm2 was 0.28 W/kg, which is less than that of the conventional (300 jxm) grain- oriented silicon steels by about 50 %.

本文言語English
ページ(範囲)3754-3756
ページ数3
ジャーナルIEEE Transactions on Magnetics
33
5 PART 2
DOI
出版ステータスPublished - 1997 12 1
外部発表はい

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Electrical and Electronic Engineering

フィンガープリント 「Reduction of iron loss in thin grain-oriented silicon steel sheets」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル