Reduction-boronation route to chromium boride (CrB) nanorods

Jianhua Ma, Yunle Gu, Liang Shi, Luyang Chen, Zeheng Yang, Yitai Qian

    研究成果: Article

    19 被引用数 (Scopus)

    抄録

    Chromium boride (CrB) nanorods were synthesized via a reduction-boronation route at 650°C in molten salt in an autoclave. The X-ray diffraction pattern of the product was indexed as the orthorhombic CrB. Transmission electron microscope images indicated that the sample consisted of single-crystalline nanorods with the diameter of 10-30 nm and a maximum length of 1.5 μm. The PL spectra showed the ultraviolet light emission at 340 nm. The thermogravimetric analysis showed that the product also had very good anti-oxidation properties below 630°C. A possible growth mechanism was proposed.

    本文言語English
    ページ(範囲)194-198
    ページ数5
    ジャーナルChemical Physics Letters
    381
    1-2
    DOI
    出版ステータスPublished - 2003 11 4

    ASJC Scopus subject areas

    • Physics and Astronomy(all)
    • Physical and Theoretical Chemistry

    フィンガープリント 「Reduction-boronation route to chromium boride (CrB) nanorods」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル