Recrystallization of Single Crystal Nickel-Based Superalloy

Bing ZHANG, Chun hu TAO, Xin LU, Chang kui LIU, Chun yan HU, Ming yuan BAI

研究成果: Article

19 引用 (Scopus)

抜粋

A series of experiments of investigating the recrystallization of single crystal DD3 superalloy were carried out. The threshold temperature for recrystallization and the effect of annealing temperature on recrystallization were studied. The results show that the threshold temperature for recrystallization of the shot-peened DD3 samples is between 1 000°C and 1 050°C under the condition of annealing for 2 h, and the recrystallization depth increases with the rise of the annealing temperature. Below 1 150°C, the recrystallization depth increases slowly with the temperature climbing, while above 1 150°C, the recrystallization depth increases quickly with the rise of the temperature. The solution of the y phase is a critical factor of the recrystallization behavior of DD3 superalloy. In addition, the kinetics and microstructural evolution of recrystallization at 1 200°C were also studied. It is found that the recrystallization progresses rapidly at 1 200°C through the growth of fully developed recrystallized grains, and the recrystallization process on the shot-peened surface is similar to that of wrought materials, including nucleation of recrystallization, growth of new grains into the matrix, and growth of new grains by swallowing up each other.

元の言語English
ページ(範囲)75-79
ページ数5
ジャーナルJournal of Iron and Steel Research International
16
発行部数6
DOI
出版物ステータスPublished - 2009 11 1
外部発表Yes

ASJC Scopus subject areas

  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント Recrystallization of Single Crystal Nickel-Based Superalloy' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用