Recrystallization behavior of hot-rolled pure tungsten and its alloy plates during high-temperature annealing

Kohei Tsuchida, Takeshi Miyazawa, Akira Hasegawa, Shuhei Nogami, Makoto Fukuda

研究成果: Article査読

55 被引用数 (Scopus)

抄録

We aimed to clarify the behavior of change in the grain structure and hardness of hot-rolled pure W and its alloys plates developed for various properties by holding at high temperature for long and short durations in the absence of irradiation. The isothermal annealing was performed at 1100 °C for 10–3115 h. The isochronous annealing was performed for 1 h in a temperature range of 1100 to 2300 °C. After heat treatment, the grain structure was observed using electron backscatter diffraction (EBSD) and the Vickers hardness was measured in the observed plane. Pure W did not recrystallize by the heat treatment for a short duration of 1 h at 1100 °C, while the recrystallization of pure W progressed during the heat treatment for long duration of 3115 h at 1100 °C. The temperature and duration at which the recrystallization occurs increase because of the dispersion of K bubbles and solid solution of Re. Considering the actual operation period of fusion reactors, a temperature of 1100 °C can result in recrystallization. It is necessary to decrease the maximum operating temperature or to use materials having a high recrystallization temperature by alloying.

本文言語English
ページ(範囲)158-163
ページ数6
ジャーナルNuclear Materials and Energy
15
DOI
出版ステータスPublished - 2018 5月

ASJC Scopus subject areas

  • 核物理学および高エネルギー物理学
  • 材料科学(その他)
  • 原子力エネルギーおよび原子力工学

フィンガープリント

「Recrystallization behavior of hot-rolled pure tungsten and its alloy plates during high-temperature annealing」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル