Properties and performance of the multi filamentary Nb3sn with ti addition processed by the nb tube method

S. Murase, H. Shiraki, M. Tanaka, M. Koizumi, H. Maeda, I. Takano, N. Aoki, M. Ichihara, E. Suzuki, K. Nota, Kazuo Watanabe, Y. Muto

研究成果: Article査読

17 被引用数 (Scopus)

抄録

MF Nb3Sn conductors made by titanium added niobium tube process have been developed for use in high fields. Composites, consisting of Nb-l.0Wt.%Ti tube with a copper sheathed tin core inside and a high conductivity copper tube outside, were stacked together up to 264 filaments, then drawn to the final sizes without any intermediate annealings. As workability was further improved by the titanium addition, it was possible to decrease the Cu/SCratio for the conductor down to 0.67 and to increase the tin concentration up to 30 wt.% in Cu-Sn inside the filament. An enhanced layer growth rate and a slightly increased grain size of Nb3Sn were observed in the titanium added conductors. compared with those made by use of pure Nb tube. The critical current density at high fields, which was more sensitive for heat-treatment condition, was superior to that of the other conventional processed conductors. Especially, the conductors with 30 % tin content have high critical current density for Nb3Sn layer and an excellent field dependence of critical current density without copper: 1550 A/mm2 at 10 T, 600 A/mm2 at 15 T and 350 A/mm2 at 17 T. The critical current was also measured in the temperature range 1.88 - 4.2 K. A coil, aiming at 14 T, was fabricated using the conductor with 25 % tin to assure high level performance in practical situations.

本文言語English
ページ(範囲)316-319
ページ数4
ジャーナルIEEE Transactions on Magnetics
21
2
DOI
出版ステータスPublished - 1985 1 1

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Electrical and Electronic Engineering

フィンガープリント 「Properties and performance of the multi filamentary Nb3sn with ti addition processed by the nb tube method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル