Production of aluminum nitride from aluminum metal using molten fluoride

Osamu Takeda, Konosuke Takagi, Takeshi Handa, Kiwamu Katagiri, Hongmin Zhu, Yuzuru Sato

研究成果: Article査読

2 被引用数 (Scopus)

抄録

The production of aluminum nitride (AlN) from aluminum metal was investigated in this study. The nitridation of Al (in rod, powder, and thin-plate forms) was facilitated by dissolving the Al2O3 thin films formed on the Al samples with a molten fluoride mixture (KF-45 mol% AlF3, KF, or LiF-50 mol% KF). AlN was formed when NH3 gas was supplied to the Al sample (in both solid and liquid forms) wetted by molten fluoride mixture. The lowest temperature at which AlN was successfully produced was 773 K. No AlN was formed when N2 or H2-25% N2 gas was supplied to the Al sample, even when a molten fluoride mixture was used. The reaction rate for the nitridation of Al powder increased with the temperature and reached 99% after 3 h at 1173 K. AlN thin films of 2-5 μm thickness were formed on Al thin plates (0.075-1.0 mm thick) at 873 K.

本文言語English
ページ(範囲)635-644
ページ数10
ジャーナルJournal of Materials Research
30
5
DOI
出版ステータスPublished - 2015 2 18

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Production of aluminum nitride from aluminum metal using molten fluoride」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル