Preparation of Ni nano-particle by rotary chemical vapor deposition

Shuhei Nakakura, Hirokazu Katsui, Takashi Goto

研究成果: Article査読

1 被引用数 (Scopus)

抄録

Carbon layer and carbon nanotube encapsuled Ni nanoparticles were prepared on a-Al2O3 support powder by rotary CVD using nickelocene as a precursor. The effect of deposition temperature (Tdep) on microstructure and compositions was investigated. The Ni content increased with increasing Tdep at 413-813 K. The highest Ni content was 2.1 mass% at 813 K. The carbon layer encapsuled Ni nanoparticlues was obtained at 613 K. Carbon nanotube encapsuled Ni nanoparticles was obtained at 893 K.