Preparation of Monodisperse ε-Fe2O3 Nanoparticles by Crystal Structural Transformation

Masafumi Nakaya, Ryo Nishida, Natsumi Hosoda, Atsushi Muramatsu

研究成果: Article査読

2 被引用数 (Scopus)

抄録

Monodisperse iron oxide nanoparticles in the ε-Fe2O3 phase, which is the rare orthorhombic phase among the four crystal systems of Fe2O3, are prepared via crystal structural transformation induced by heat treatment of SiO2-coated monodisperse FeO nanoparticles. The mean diameter of the resulting ε-Fe2O3 nanoparticles is 41.0 ± 4.2 nm. Compared with the as-synthesized 40.9 ± 3.8 nm-FeO nanoparticles, which are used as the precursor, the size and size distribution of the nanoparticles remain almost unchanged after heat treatment. By optimizing the thickness of the SiO2 shell, coalescence of the nanoparticles during heat treatment can be prevented. XRD measurements do not detect the α-Fe2O3 phase and γ-Fe2O3 phase in the obtained sample. The resulting ε-Fe2O3 nanoparticles exhibit a high coercivity of 23.4 kOe at room temperature.

本文言語English
論文番号1700110
ジャーナルCrystal Research and Technology
52
11
DOI
出版ステータスPublished - 2017 11

ASJC Scopus subject areas

  • 化学 (全般)
  • 材料科学(全般)
  • 凝縮系物理学

フィンガープリント

「Preparation of Monodisperse ε-Fe<sub>2</sub>O<sub>3</sub> Nanoparticles by Crystal Structural Transformation」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル