Ag/Yb0.35Co4Sb12热电复合材料的制备及热电性能研究

Zhen Xing Zhou, Peng Chen, Sheng Jie Fan, Xiao Fang Lu, Shi Jia Gu, Lian Jun Wang

研究成果: Article査読

1 被引用数 (Scopus)

抄録

As a high-performance medium-temperature zone thermoelectric material, skutterudites has attracted much attention. Recently, how to further improve its thermoelectric performance has become a hot and difficult topic. Here, TE composites incorporated with different content silver are fabricated via "Melting-annealing" at high temperature and Spark Plasma Sintering (SPS). The influence about introduced Ag into matrix was studied carefully. As a result, the composites include Ag shows remarkably improved electrical conductivity (σ). In addition, the absolute value of Seebeck coefficient (α) was significantly increased due to the influence of the energy filtering effect at the interface between skutterudites and Ag, and the increase of thermal conductivity (κ) was also effectively controlled. Finally, the thermoelectric properties were greatly improved. Specially, when the Ag content was 0.5wt%, the maximal ZT values reached 1.28 at 800 K, which is approximately 44.3% higher than the matrix.

寄稿の翻訳タイトルPreparation and Thermoelectric Properties of Ag/Yb0.35Co4Sb12 Thermoelectric Composites
本文言語!!
ページ(範囲)196-200 and 206
ジャーナルRengong Jingti Xuebao/Journal of Synthetic Crystals
48
2
出版ステータスPublished - 2019 2 1
外部発表はい

ASJC Scopus subject areas

  • セラミックおよび複合材料
  • 凝縮系物理学
  • 材料化学

フィンガープリント

「Ag/Yb<sub>0.35</sub>Co<sub>4</sub>Sb<sub>12</sub>热电复合材料的制备及热电性能研究」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル