Preparation and magnetization of hematite nanocrystals with amorphous iron oxide layers by hydrothermal conditions

G. S. Li, R. L. Smith, H. Inomata, K. Arai

研究成果: Article査読

26 被引用数 (Scopus)

抄録

Hematite nanocrystals modified with surface layers of amorphous hydrous iron oxides were prepared by hydrothermal conditions in the absence of alkali. The formation temperature was found to be ca. 130°C. When the temperature was lower than 130°C, no product was formed, while above this temperature, the amount of amorphous hydrous iron oxides at the surface of hematite nanocrystals was drastically decreased. The amorphous layers on the hematite nanocrystals obtained at 130°C were determined to be Fe2O3·1.64H2O. The coercivity for the hematite nanocrystals with modified layers was 0.534 kOe, which is slightly larger than the values for hematite nanocrystals with few agglomerations.

本文言語English
ページ(範囲)949-955
ページ数7
ジャーナルMaterials Research Bulletin
37
5
DOI
出版ステータスPublished - 2002 4 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Preparation and magnetization of hematite nanocrystals with amorphous iron oxide layers by hydrothermal conditions」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル