PRECIPITATION BEHAVIOR OF MnS AND Ca-CONTAINING INCLUSIONS IN Ca-ADDED CC SLAB.

Shin ya Kitamura, Ko Miyamura, Isahiro Fukuoka

研究成果: Article査読

3 被引用数 (Scopus)

抄録

Using an X-ray microanalyzer (CMA), MnS precipitation behavior and the distribution of Ca oxide and sulfide were investigated. The amount of MnS measured did not have good correspondence with previously reported parameters to suppress MnS formation. In the slab of which the oxygen content was too high to expect the formation of CaS in molten steel, S was observed in or around the calcium aluminate and the amount of MnS decreased. The calcium aluminate in which S was highly enriched was mainly observed at the segregated interdendritic region. The desulfurization reaction by calcium-aluminate occurs easily with solidification.

本文言語English
ページ(範囲)344-350
ページ数7
ジャーナルTransactions of the Iron and Steel Institute of Japan
27
5
DOI
出版ステータスPublished - 1987 1 1
外部発表はい

ASJC Scopus subject areas

  • Engineering(all)

フィンガープリント 「PRECIPITATION BEHAVIOR OF MnS AND Ca-CONTAINING INCLUSIONS IN Ca-ADDED CC SLAB.」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル