Precipitation behavior of alloy nitrides during plasma nitriding in Fe-0.6mass%C-1mass%M (M=Al, Cr) martensitic steels

Yusaku Tomio, Shigeki Kistuya, Goro Miyamoto, Tadashi Furuhara

研究成果: Conference contribution

抄録

Change in surface hardness and precipitation of alloy nitrides in Fe-0.6C binary and Fe-0.6C-1M(M=A1, Cr) (mass%) ternary martensitic steels during plasma nitriding was investigated by means of hardness test, scanning electron microscopy and transmission electron microscopy. In the Fe-0.6C binary alloy, surface hardness is hardly increased by nitriding at 823K. On the other hand, in Fe-0.6C-1A1 and Fe-0.6C-lCr alloys the surface hardness increases largely and reaches HV650 and HV550, respectively. In the Fe-0.6C-1A1 alloy, fine NaCl type A1N platelets of which length is about l00nm and thickness is a few nm, precipitate mainly on dislocation lying on {001} planes of the matrix inside martensite laths holding Baker-Nutting orientation relationship with respect to ferrite matrix. In the Fe-0.6C-lCr alloy, NaCl type CrN platelets about 20nm in length and several atomic layers in thickness precipitate much more uniformly than in the Fe-0.6C-1A1 alloy also on {001} planes of the matrix. Those precipitate phases in Fe-0.6C-1M ternary martensite are similar to those in Fe-M ferritic binary alloys reported previously. A1N dispersion in martensite is finer due to higher density of dislocation as nucleation sites, resulting higher hardness density, than in ferrite. On the other hand, hardness of martensite is lower than ferrite presumably due to coarser dispersion of CrN resulted from in-situ transition of Cr-rich cementite to CrN and less amount finer CrN platelets..

本文言語English
ホスト出版物のタイトルProceedings of the 17th IFHTSE Congress
出版社The Japan Society for Heat Treatment (JSHT)
ページ161-164
ページ数4
ISBN(電子版)9780000000002
出版ステータスPublished - 2009 1 1
イベント17th International Federation for Heat Treatment and Surface Engineering Congress 2008, IFHTSE 2008 - Kobe, Japan
継続期間: 2008 10 262008 10 28

出版物シリーズ

名前Proceedings of the 17th IFHTSE Congress
1

Other

Other17th International Federation for Heat Treatment and Surface Engineering Congress 2008, IFHTSE 2008
国/地域Japan
CityKobe
Period08/10/2608/10/28

ASJC Scopus subject areas

  • 表面、皮膜および薄膜
  • 凝縮系物理学
  • 材料力学

フィンガープリント

「Precipitation behavior of alloy nitrides during plasma nitriding in Fe-0.6mass%C-1mass%M (M=Al, Cr) martensitic steels」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル