Precipitation behavior of a novel cobalt-based superalloy subjected to prior plastic deformations

Huakang Bian, Yunping Li, Daixiu Wei, Yujie Cui, Fenglin Wang, Shihai Sun, Kenta Yamanaka, Yuichiro Koizumi, Akihiko Chiba

研究成果: Article査読

16 被引用数 (Scopus)

抄録

The precipitation behavior of a novel cobalt-based superalloy subjected to prior plastic deformations was investigated in details by using field emission scanning electron microscope (FE-SEM), transmission electron microscope (TEM), etc. The precipitation of a μ-phase, which appeared at temperatures of 1073–1373 K, was confirmed, while MC-type carbide was observed at the temperatures > 1173 K. The prior plastic deformations promoted the precipitation of the μ-phase during subsequent aging. Further, the precipitation of the μ-phase at temperatures lower than 1173 K was confirmed to occur predominantly along the {111} slip bands; this was the dominant deformation mechanism of this alloy during plastic deformation. In contrast, there was no evidence that the precipitation of the MC-type carbide was affected by the prior plastic deformations in the case of the specimens exposed at 1273 and 1373 K.

本文言語English
ページ(範囲)1-10
ページ数10
ジャーナルMaterials and Design
112
DOI
出版ステータスPublished - 2016 12 15

ASJC Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Precipitation behavior of a novel cobalt-based superalloy subjected to prior plastic deformations」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル