Phase transformations in the B2 phase of Co-rich Co-Al binary alloys

K. Niitsu, T. Omori, M. Nagasako, K. Oikawa, R. Kainuma, K. Ishida

研究成果: Article

10 引用 (Scopus)

抜粋

Phase transformations in the β (B2) phase of Co-21 and -23 at.% Al alloys were examined using transmission electron microscopy, energy dispersive X-ray spectroscopy and differential scanning calorimetry. The microstructures obtained from as-quenched specimens were found to be strongly affected by the quenching condition. While relatively thick sheet-specimens with a lower quenching rate showed bainitic plate precipitates with a fcc structure, a martensite-like structure was observed by optical microscopy in relatively thin specimens with a higher quenching rate. Regardless of the quenching condition, a spinodal-like microstructure composed of A2 and B2 phases was also detected and the A2 phase changed to a metastable hcp phase during further aging.

元の言語English
ページ(範囲)2697-2702
ページ数6
ジャーナルJournal of Alloys and Compounds
509
発行部数6
DOI
出版物ステータスPublished - 2011 2 10

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント Phase transformations in the B2 phase of Co-rich Co-Al binary alloys' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用