Phase transformation and magnetic properties of ferromagnetic Cu-Mn-Ga alloys

Takuro Kushima, Koichi Tsuchiya, Yasukazu Murakami, Daisuke Shindo, Yoshikazu Todaka, Minoru Umemoto

    研究成果: Article査読

    2 被引用数 (Scopus)

    抄録

    Phase transformation, microstructure and magnetic properties of Cu-(11-14)mol%Mn-20 mol%Ga alloy were investigated. Magnetic domain structures were also investigated by the Lorentz microscopy and electron holography. Plate-like martensite phase (ζ M. ordered hep) was observed in as-quenched Cu-12 mol%Mn-20 mol%Ga. Phase transformation from ζ M martensite to ζ phase (hcp) occurred at around 540 K on heating. The ζ phase decomposed into β (ordered hcp) and β(bcc) phase at around 700 K, then became the single β phase at around 840 K. By subsequent slow cooling, ζ phase was observed at room temperature. Results of the Lorentz microscopy and electron holography revealed that the twin plates of CM martensite and magnetic domains have one-to-one correspondence, suggesting high magneto-crystalline anisotropy energy of the martensite phase. Saturation magnetization and Curie temperature increased with Mn content.

    本文言語English
    ページ(範囲)849-855
    ページ数7
    ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
    70
    10
    DOI
    出版ステータスPublished - 2006 10月

    ASJC Scopus subject areas

    • 凝縮系物理学
    • 材料力学
    • 金属および合金
    • 材料化学

    フィンガープリント

    「Phase transformation and magnetic properties of ferromagnetic Cu-Mn-Ga alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル