Phase equilibria in the Ni-Mn-In alloy system

T. Miyamoto, M. Nagasako, R. Kainuma

研究成果: Article査読

16 被引用数 (Scopus)

抄録

Phase equilibria at 700 and 850 °C, critical temperatures of B2/L2 1 order-disorder transformation and martensitic and ferromagnetic phase regions at room temperature in the Ni-Mn-In system were determined mainly by diffusion triple method using a two-stage diffusion couple technique. It was confirmed that a single phase region of the β phase at both 700 and 850 °C exists in a wide composition range along the NiMn-NiIn section and that the L21 ordered phase region appears in the vicinity of Ni 2MnIn in the temperature region below about 800 °C. The composition lines, iso-Ms and iso-TFM, possessing the Ms and TC temperatures at room temperature, respectively, were successfully estimated and the coincidence between the iso-Ms and iso-TFM was confirmed in the composition region from 10 to 20 at.% In in the β-phase region.

本文言語English
ページ(範囲)57-63
ページ数7
ジャーナルJournal of Alloys and Compounds
549
DOI
出版ステータスPublished - 2013 2月 5

ASJC Scopus subject areas

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Phase equilibria in the Ni-Mn-In alloy system」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル