Perpendicular magnetic anisotropy and domain structure of L10-ordered FePt films fabricated by monatomic layer control

T. Shima, T. Moriguchi, S. Mitani, K. Takanashi, H. Ito, S. Ishio

研究成果: Conference article査読

12 被引用数 (Scopus)


Magnetic domain structures and perpendicular magnetic anisotropies for L10-ordered FePt alloy films have been investigated. The films were prepared by alternating Fe (001) and Pt (001) monatomic layers on MgO (001) substrates at low temperatures below 230 °C. In addition to the fundamental (002) peak, (001) and (003) superlattice peaks have clearly been observed in the X-ray diffraction patterns, indicating the formation of L10-ordered structure. The magnetization measurements show that all the samples are perpendicularly magnetized. Good magnetic squareness (Mr/Ms∼0.9) from the magnetization curves are obtained and highly interconnected stripe domain patterns are observed for the samples grown at Ts ≥ 160 °C.

ジャーナルIEEE Transactions on Magnetics
5 I
出版ステータスPublished - 2002 9
イベント2002 International Magnetics Conference (Intermag 2002) - Amsterdam, Netherlands
継続期間: 2002 4 282002 5 2

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 電子工学および電気工学


「Perpendicular magnetic anisotropy and domain structure of L1<sub>0</sub>-ordered FePt films fabricated by monatomic layer control」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。